Diameter
(mm)
|
Tolerance
(mm)
|
Tensile Strength
(N/mm2) |
Min.Torsion
(N0/100d) |
Min. Bending
(N0) |
Knotted Rate
(≥%) |
Elongation
(≥%) |
Brass Mass (g/kg) |
Cu Content
(%) |
0.20 |
±0.010 |
2150-2450
2450-2750
2750-3050
3050-3350 |
41
41
41
35 |
125
125
125
125 |
58
58
50
50 |
1.6 |
3.5—5.5 |
64—71.5 |
0.22 |
2150-2450
2450-2750
2750-3050
3050-3350 |
41
41
38
32 |
125
125
125
125 |
58
58
50
50 |
0.25 |
2150-2450
2450-2750
2750-3050
3050-3350 |
41
41
40
30 |
125
125
105
75 |
58
58
50
50 |
0.28 |
2150-2450
2450-2750
2750-3050
3050-3350 |
40
40
35
30 |
115
105
85
65 |
58
58
50
50 |
0.295 |
2150-2450
2450-2750
2750-3050
3050-3350 |
40
39
33
28 |
105
100
85
65 |
58
58
50
50 |
0.30 |
2150-2450
2450-2750
2750-3050
3050-3350 |
40
39
31
25 |
105
100
85
65 |
58
58
50
50 |
0.32 |
2150-2450
2450-2750
2750-3050
3050-3350
|
39
38
30
25
|
90
85
75
65
|
58
58
50
50
|
0.33 |
±0.015 |
2150-2450
2450-2750
2750-3050
3050-3350
|
37
35
30
25
|
80
75
65
55
|
58
58
50
50
|
|
|
|
0.35 |
2450-2750
2750-3050
3050-3350
|
35
30
25
|
60
55
50
|
58
50
50
|
|
|
|
0.38 |
2150-2450
2450-2750
2750-3050
3050-3350
|
35
35
30
20
|
65
65
55
50
|
58
58
50
50
|
|
|
|
0.40 |
2150-2450
2450-2750
2750-3050
3050-3350
|
35
35
30
20
|
55
55
50
45
|
58
58
50
50
|
|
|
|
0.45 |
2150-2450
2450-2750
2750-3050
|
30
30
25
|
45
45
40
|
58
58
50
|
1.8 |
3.0—5.0 |
0.50 |
2150-2450
2450-2750
2750-3050
|
30
30
25
|
40
35
30
|
50
50
50
|
1.9 |
0.56 |
2150-2450
2450-2750
2750-3050
|
28
28
24
|
35
30
25
|
50
50
50
|
1.9 |
0.60 |
2150-2450
2450-2750
|
30
28
|
30
28
|
50
50
|
2.0 |
0.65 |
2150-2450
2450-2750
2750-3050
|
27
27
25
|
27
27
25
|
50
50
50
|
2.2 |
0.70 |
2150-2450
2450-2750
2750-3050
|
25
25
24
|
25
25
24
|
50
50
50
|